•   LLDPE / linear low density polyethylene virgin and recycle granules 
  •   LLDPE / linear low density polyethylene virgin and recycle granules 
  •   LLDPE / linear low density polyethylene virgin and recycle granules 

  LLDPE / linear low density polyethylene virgin and recycle granules 

  • Melt Flow Rate (MFR): 20 g/10min
  • Density: 0.924 g/cm3
  • Elongation at Yield: 13%
  • Elongation at Break: 200%
  • Dark Drop Impact: 105g

We're here to help:

Easy ways to get the answers you need.

(※ Click this button to inquiry)
share with :
Detergent Surfactant Agent
Chlor-Alkali Chemicals
Agriculture & Feed and Food Additive
Electronic Chemical Raw Materials
Water Treatment Chemicals
Mining Chemical Auxiliaries
Leather Textile Auxiliaries
Oilfield Chemicals
Glass Ceramic Chemicals
Coating and Resin Chemicals
Phosphate Chemicals
Plasticizer and Rubber Chemicals

sale@orichemical.com

+86 371 -5369 2015
+86 371 -5369 2016

+86 371 -6808 5477

■ Specifications
                    Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
 
Tests Value Unit
Melt Flow Rate (MFR) 2.0± 0.4 g/10min
Density 920± 2 Kg/cm3
Tensile Strengthat Yield 8 Mpa &ge
Tensile Strengthat Break 12 Mpa &ge
haze 15 %&le
Packing In 25 kg PP woven bags,20MT/20&rsquo FCL
■ Full Data
     
Melt Flow Rate (MFR) 20 g/10min
Density 0.924 g/cm3
Tensile Strength MD12 Mpa
TD 10
Elongation at Yield 13 %
Elongation at Break 200
Dark Drop Impact 105 g
Brittle Temperature(F 50) -70 ° C
Vicat Softening Point 90 ° C
Packing In 25 kg wovenbags,20MT/20&rsquo FCL

Powder Rotational Molding Grade  

Tests Value Unit
Melt Flow Rate (MFR) 3.2 g/10min
Density 0.939 g/cm3
Melting Point 127 ° C
Tensile Yield Strength 21 Mpa
Tensile Strength at Break 28 Mpa
Elongation at Break 1,100 %
Flexural Modulus 750 Mpa
Brittle Temperature < -60 ° C
Inquiry >>